A foundry is a factory that produces metal castings. Metals are cast into shapes by melting them into a liquid, pouring the metal in a mold, and removing the mold material or casting after the metal has solidified as it cools. The most common metals processed are aluminium and cast iron. However, other metals, such as bronze, brass, steel, magnesium, and zinc, are also used to produce castings in foundries. In this process, parts of desired shapes and sizes can be formed.
In metalworking, casting involves pouring liquid metal into a mold, which contains a hollow cavity of the desired shape, and then allowing it to cool and solidify. The solidified part is also known as a casting, which is ejected or broken out of the mold to complete the process. Casting is most often used for making complex shapes that would be difficult or uneconomical to make by other methods.
Melting metal in a crucible for casting
Melting is performed in a furnace. Virgin material, external scrap, internal scrap, and alloying elements are used to charge the furnace. Virgin material refers to commercially pure forms of the primary metal used to form a particular alloy. Alloying elements are either pure forms of an alloying element, like electrolytic nickel, or alloys of limited composition, such as ferroalloys or master alloys. External scrap is material from other forming processes such as punching, forging, or machining. Internal scrap consists of gates, risers, defective castings, and other extraneous metal oddments produced within the facility.
The process includes melting the charge, refining the melt, adjusting the melt chemistry and tapping into a transport vessel. Refining is done to remove deleterious gases and elements from the molten metal to avoid casting defects. Material is added during the melting process to bring the final chemistry within a specific range specified by industry and/or internal standards. Certain fluxes may be used to separate the metal from slag and/or dross and degassers are used to remove dissolved gas from metals that readily dissolve certain gasses. During the tap, final chemistry adjustments are made.
Several specialised furnaces are used to melt the metal. Furnaces are refractory lined vessels that contain the material to be melted and provide the energy to melt it. Modern furnace types include electric arc furnaces (EAF), induction furnaces, cupolas, reverberatory, and crucible furnaces. Furnace choice is dependent on the alloy system quantities produced. For ferrous materials EAFs, cupolas, and induction furnaces are commonly used. Reverberatory and crucible furnaces are common for producing aluminium, bronze, and brass castings.
Furnace design is a complex process, and the design can be optimized based on multiple factors. Furnaces in foundries can be any size, ranging from small ones used to melt precious metals to furnaces weighing several tons, designed to melt hundreds of pounds of scrap at one time. They are designed according to the type of metals that are to be melted. Furnaces must also be designed based on the fuel being used to produce the desired temperature. For low temperature melting point alloys, such as zinc or tin, melting furnaces may reach around 500° C. Electricity, propane, or natural gas are usually used to achieve these temperatures. For high melting point alloys such as steel or nickel based alloys, the furnace must be designed for temperatures over 1600° C. The fuel used to reach these high temperatures can be electricity (as employed in electric arc furnaces) or coke.
The majority of foundries specialize in a particular metal and have furnaces dedicated to these metals. For example, an iron foundry (for cast iron) may use a cupola, induction furnace, or EAF, while a steel foundry will use an EAF or induction furnace. Bronze or brassfoundries use crucible furnaces or induction furnaces. Most aluminium foundries use either electric resistance or gas heated crucible furnaces or reverberatory furnaces.
In the case of aluminium alloys, a degassing step is usually necessary to reduce the amount of hydrogen dissolved in the liquid metal. If the hydrogen concentration in the melt is too high, the resulting casting will be porous as the hydrogen comes out of solution as the aluminium cools and solidifies. Porosity often seriously deteriorates the mechanical properties of the metal.
An efficient way of removing hydrogen from the melt is to bubble argon or nitrogen through the melt. To do that, several different types of equipment are used by foundries. When the bubbles go up in the melt, they catch the dissolved hydrogen and bring it to the top surface. There are various types of equipment which measure the amount of hydrogen present in it. Alternatively, the density of the aluminium sample is calculated to check amount of hydrogen dissolved in it.
In cases where porosity still remains present after the degassing process, porosity sealing can be accomplished through a process called metal impregnating.
Diagrams of two pattern types
A diagram of draft on a pattern
A diagram of an undercut in a mold
In the casting process a pattern is made in the shape of the desired part. Simple designs can be made in a single piece or solid pattern. More complex designs are made in two parts, called split patterns. A split pattern has a top or upper section, called a cope, and a bottom or lower section called a drag. Both solid and split patterns can have cores inserted to complete the final part shape. Cores are used to create hollow areas in the mold that would otherwise be impossible to achieve. Where the cope and drag separates is called the parting line.
When making a pattern it is best to taper the edges so that the pattern can be removed without breaking the mold. This is called draft. The opposite of draft is an undercut where there is part of the pattern under the mold material, making it impossible to remove the pattern without damaging the mold.
The pattern is made out of wax, wood, plastic or metal. The molds are constructed by several different processes dependent upon the type of foundry, metal to be poured, quantity of parts to be produced, size of the casting and complexity of the casting. These mold processes include:
- Sand casting — Green or resin bonded sand mold.
- Lost-foam casting — Polystyrene pattern with a mixture of ceramic and sand mold.
- Investment casting — Wax or similar sacrificial pattern with a ceramic mold.
- Ceramic mold casting — Plaster mold.
- V-process casting — Vacuum is used in conjunction with thermoformed plastic to form sand molds. No moisture, clay or resin is needed for sand to retain shape.
- Die casting — Metal mold.
- Billet (ingot) casting — Simple mold for producing ingots of metal normally for use in other foundries.
In a foundry, molten metal is poured into molds. Pouring can be accomplished with gravity, or it may be assisted with a vacuum or pressurized gas. Many modern foundries use robots or automatic pouring machines for pouring molten metal. Traditionally, molds were poured by hand using ladles.
The solidified metal component is then removed from its mold. Where the mold is sand based, this can be done by shaking or tumbling. This frees the casting from the sand, which is still attached to the metal runners and gates - which are the channels through which the molten metal traveled to reach the component itself.
Degating is the removal of the heads, runners, gates, and risers from the casting. Runners, gates, and risers may be removed usingcutting torches, bandsaws or ceramic cutoff blades. For some metal types, and with some gating system designs, the sprue, runners and gates can be removed by breaking them away from the casting with a sledge hammer or specially designed knockout machinery. Risers must usually be removed using a cutting method (see above) but some newer methods of riser removal use knockoff machinery with special designs incorporated into the riser neck geometry that allow the riser to break off at the right place.
The gating system required to produce castings in a mold yields leftover metal, including heads, risers and sprue, sometimes collectively called sprue, that can exceed 50% of the metal required to pour a full mold. Since this metal must be remelted as salvage, the yield of a particular gating configuration becomes an important economic consideration when designing various gating schemes, to minimize the cost of excess sprue, and thus melting costs.
Heat treating is a group of industrial and metalworking processes used to alter the physical, and sometimes chemical, properties of a material. The most common application is metallurgical. Heat treatments are also used in the manufacture of many other materials, such as glass. Heat treatment involves the use of heating or chilling, normally to extreme temperatures, to achieve a desired result such as hardening or softening of a material. Heat treatment techniques include annealing, case hardening, precipitation strengthening, tempering and quenching. It is noteworthy that while the term heat treatment applies only to processes where the heating and cooling are done for the specific purpose of altering properties intentionally, heating and cooling often occur incidentally during other manufacturing processes such as hot forming or welding.